T-VCP-33557 Black EMERALD 3000 FR BLACK BASE BRIGHT

% Specific Color Heat BROWN 83MB01 (c) Iron Oxide, Tan HR 60 1.78 PBr-11 1 I/O SBR 83MB02 (c) Iron Oxide, Light 68 2.1 PBr-6 2 C I/O SBR 83MB03 (c) Iron Oxide, Dark 60 1.83 PBr-6 2 C I/O SBR 83EP02 Iron Oxide, Light 69 1.98 PBr-6 2 C I/O EPDM 83EP03 Iron Oxide, Dark 69 1.98 PBr-6 2 C I/O EPDM BLACK 90MB01 (c) Furnace N-330 31 1.2 PBk-7 1 I/O SBR 90MB05 (c) Iron Oxide 60 1.8 PBk-11 2 C I/O SBR 90EP01 Furnace Black 33 1.05 PBk-7 1 I/O EPDM 90EP05 Iron Oxide 55 1.56 PBk-11 2 C I/O EPDM ALUMINUM 61MB01 Aluminum 70 1.5 PM-1 1 I/O SBR 61EP01 Aluminum 60 1.31 PM-1 1 I/O EPDM RS = Red Shade YS = Yellow Shade VYS = Very Yellow Shade BS = Blue Shade VBS = Very Blue Shade GS = Green Shade NC = Non-Crystallizing HR = Heat-Resistant (a) = Potential Migration at Low Use Levels (b) = Poor Alkali Resistance - Not Recommended for Open Steam Cure (c) = Six Month Shelf Life LIGHTFASTNESS I = Indoor Only I/O = Indoor or Outdoor Mass = Outdoor Masstone Application Only C = Some Caution Advised HEAT STABILITY 1 = Above 400°F 2 = 350°F–400°F 3 = Below 350°F C = Some Caution Advised 1.844.4AVIENT www.avient.com Copyright © 2024, Avient Corporation.

70-PU-121 PURPLE BLACK PP FR 8-6 LMS-1000

HDPE is not recommended for purging as it can cause delamination or lead to black specks. Runners • Full-round runners or modified trapezoid runners are the best designs. • Half-round runners are not recommended. • Only naturally balanced runner systems (“H” pattern) are recommended. • Runner diameters should not be less than the part thickness. • Runner diameter should be 1.5x the part thickness. • Step each 90° bend in the system down in size. • Place vents at each 90° intersection and vent to atmosphere. • Hot runner molds are acceptable and should be sized by the manufacturer. Sink Marks Melt too hot Insufficient material volume • Increase shot size • Increase packing pressure Part geometry too thick • Reduce wall thickness • Reduce rib thickness Flash Injection pressure too high • Decrease injection pressure • Increase clamp pressure • Increase transfer position Excess material volume • Decrease pack pressure • Decrease shot size Melt and/or mold temperature too hot Loose clamp • Reset mold height • Increase clamp tonnage Shrink Too much shrink • Increase cooling time Too little shrink • Decrease cooling time Burning • Reduce decompression • Clean, widen and increase number of vents • Increase gate size to reduce shear Wet material • Verify material is dried at proper condition Nozzle Drool Nozzle temperature too hot • Decrease nozzle temperature • Decrease back pressure • Increase screw decompression • Verify material has been dried at proper conditions Incorrect nozzle • Use reverse taper tip Weld Lines Melt front temperatures are too low • Increase pack and hold pressure • Increase gate size • Identify end of fill pattern and verify proper vent location • Add vents or increase vent width • Move gate location Warp • Reduce injection speed • Increase pack pressure • Increase pack time • Increase cool time Mold design • Non-uniform mold cooling Part design • Non-uniform wall thickness Thermolator incorrect temperature • Check settings • Inspect thermocouple Sticking in Mold Overfilled cavity • Decrease injection rate and pressure • Decrease hold pressure • Decrease cooling time Part too hot • Decrease barrel temperature • Increase cooling time • Increase draft angle • Polish cores in direction of ejection Black Specks Contamination • Purge machine Degradation • Reduce melt temperature • Reduce screw speed • Reduce back pressure Machine related • Check for wear on screw, barrel or check ring Delamination • Purge barrel to eliminate material contamination • Reduce sharp corners in material flow path • Increase venting Discoloration Oversheared material • Decrease melt temperature • Reduce residence time Mold design • Increase gate sizing Dry material • Check moisture of material to ensure it is within the recommended moisture percentage for molding 1.844.4AVIENT www.avient.com Copyright © 2021, Avient Corporation.

STAN-TONE HCC-34803 BCI T-VEN GRAN GEON 87703 BLACK 2880 PP FR 8-6 LMS-1000

PARENT ZHEA CDB210 T.12 BLACK TPV PP FR 8-6 LMS-1000

BLACK ACRYLIC E&T PLASTICS-BLUE ABS PP FR 8-6 LMS-1000

F169A BLACK-HV BLUE # 4 T-225-3-3 PP FR 8-6 LMS-1000

BLACK SMOKE STAN-TONE HCC-34765 BCI T-GRANITE PP FR 8-6 LMS-1000

T BLUE 3M BLACK 3 PP FR 8-6 LMS-1000