EDGETEK™ POLYETHERETHERKETONE (PEEK) HIGH PERFORMING MELT-PROCESSABLE POLYMER PRODUCT SELECTION GUIDE Edgetek™ Polyetheretherketone (PEEK) HIGH PERFORMING MELT-PROCESSABLE POLYMER PROPERTY CONDITIONS TEST METHOD UNITS EDGETEK™ ET9800-0001 EM EDGETEK™ ET9800-0002 RS EDGETEK™ ET9800-0003 RS EDGETEK™ ET9800-0004 RS EC LUBRIONE™ LB9800-0001 AR PHYSICAL Mold Shrinkage - Transverse – ASTM D955 in/in 0.014 0.010 0.011 0.009 0.014 MECHANICAL Tensile Strength - Yield – ASTM D638 PSI 14425 15640 23680 36500 19700 Tensile Elongation - Yield – ASTM D638 % 5.4 3.0 2.2 1.5 0.2 Tensile Elongation - Break – ASTM D638 % 19.5 3.1 2.2 1.5 1.9 Tensile Modulus – ASTM D638 PSI 555150 827700 1591300 5301000 2285600 Flexural Modulus – ASTM D790 PSI 529300 690700 1418300 3084300 1443400 Flexural Strength – ASTM D790 PSI 23500 27300 36000 52100 30300 IMPACT Izod, Notched – ASTM D256 ft-lbs/in 1.0 0.7 1.1 1.3 0.6 Izod, Unnotched – ASTM D256 ft-lbs/in N.B. 13.1 15.3 13.8 5.0 THERMAL Melting Point – – °C 343 343 343 343 343 Glass Transition (DSC) – – °C 143 143 143 143 143 Heat Deflection Temp 264 psi, Unannealed ASTM D648 °C 151 178 320 325 > 300 CLTE, Flow Direction 23°C to 140°C ASTM E831 cm/cm/°C 4.0E-05 5.5E-05 2.2E-05 7.0E-06 1.9E-05 CLTE, Flow Direction 140°C to 250°C ASTM E831 cm/cm/°C 9.7E-05 7.8E-05 2.3E-05 6.5E-06 2.2E-05 Polyetheretherketone (PEEK) is widely considered to be one of the highest performing melt-processable polymers in the industry.

FIBER OPTICAL CABLES MOVING HIGH PERFORMANCE FIBERS FORWARD Molecular Structure Chemical Name Cured Phenol-Aldehyde from melt-spun Novalac resin. The precursor resin is melt-spun in a solution of formaldehyde and hydrochloric acid. Abrasion Resistance Ultraviolet (UV) Resistance Flame Resistance Chemical Resistance (Acid Chemical Resistance (Alkali) Chemical Resistance (Organic Solvent) Strength Retention (H2O) O P P P P P P Property UOM Value Breaking Tenacity g/d 1.5 Specific Gravity Ratio 1.27 Elongation @ Break % 30.0 - 40.0 Tensile Modulus g/d 2.5 - 5.0 Moisture Regain* % 6.0 Creep** % N/A Shrinkage*** % < 0.1 Melt Point °C N/A Decomposition Temp.

FIBER-LINE™ High Performance Synthetic Fibers PRODUCT SELECTION GUIDE FIBER-LINE™ HIGH PERFORMANCE SYNTHETIC FIBERS Kevlar® Para-Aramid Nomex® Meta-Aramid Vectran® LCP Zylon® PBO Carbon Fiber UHMWPE PET Polyester Fiberglass Novoloid Technora® Filament Yarn TECHNICAL PROPERTIES Standard Modulus High Modulus Standard Modulus Standard Modulus High Modulus Standard Modulus High Modulus Standard Modulus Standard Modulus High Modulus High Tenacity Low Shrink E-Glass S-Glass Standard Modulus Standard Modulus Breaking Tenacity (g/d) 23.0 23.6 5.0 23.0 30.0 42.0 42.0 23.0 28.0 38 9.3 8.4 6.0 - 7.3 6.7 - 9.4 1.5 28.0 Specific Gravity (Ratio) 1.44 1.44 1.38 1.40 1.40 1.54 1.56 1.80 0.97 0.97 1.38 1.38 2.58 2.48 1.27 1.39 Elongation at Break (%) 3.5 2.5 30.0 3.8 2.8 3.5 2.5 1.5 3.5 3.1 14.6 19.5 3.5 5.5 30.0 - 40.0 4.6 Tensile Modulus (g/d) 555 885 125 600 830 1200 1800 1480 850 1250 120 70 200–275 140–170 2.5–5.0 590 Equilibrium Moisture Regain at 55% RH (%) 5.0 5.0 4.5

70° C  22 hrs, 70 hrs, 168 hrs (1 week), 1000 hrs (42 days) 121° C  22 hrs, 70 hrs, 168 hrs (1 week), 1000 hrs (42 days) Softening/melt temperatures vary with polymer type and grade.

70° C  22 hrs, 70 hrs, 168 hrs (1 week), 1000 hrs (42 days) 121° C  22 hrs, 70 hrs, 168 hrs (1 week), 1000 hrs (42 days) Softening/melt temperatures vary with polymer type and grade.

BLACK C PP CC10075659 GOLD PBT CC10105686 BROWN PBT

BLUE # 4 T-225-3-3 PE CYAN BLUE C

PINK 225 PURPLE C

BLUE 225-2-5 C GREEN LM

LC AB1-225 FANATICS 872 C UB