Colorant Chromatics™ Conductive Formulations Stat-Tech™ Static Dissipative & Electrically Conductive Formulations Therma-Tech™ Thermally Conductive Formulations

Drop all heating sections 50°F–100°F during extended downtime, die changes, etc. or keep bleeding if possible. You have the responsibility to conduct full-scale end-product performance testing to determine suitability in your application, and you assume all risk and liability arising from your use of the information and/or use or handling of any product. You have the responsibility to conduct full-scale end-product performance testing to determine suitability in your application, and you assume all risk and liability arising from your use of the information and/or use or handling of any product.

EDGETEK™ POLYETHERETHERKETONE (PEEK) HIGH PERFORMING MELT-PROCESSABLE POLYMER PRODUCT SELECTION GUIDE Edgetek™ Polyetheretherketone (PEEK) HIGH PERFORMING MELT-PROCESSABLE POLYMER PROPERTY CONDITIONS TEST METHOD UNITS EDGETEK™ ET9800-0001 EM EDGETEK™ ET9800-0002 RS EDGETEK™ ET9800-0003 RS EDGETEK™ ET9800-0004 RS EC LUBRIONE™ LB9800-0001 AR PHYSICAL Mold Shrinkage - Transverse – ASTM D955 in/in 0.014 0.010 0.011 0.009 0.014 MECHANICAL Tensile Strength - Yield – ASTM D638 PSI 14425 15640 23680 36500 19700 Tensile Elongation - Yield – ASTM D638 % 5.4 3.0 2.2 1.5 0.2 Tensile Elongation - Break – ASTM D638 % 19.5 3.1 2.2 1.5 1.9 Tensile Modulus – ASTM D638 PSI 555150 827700 1591300 5301000 2285600 Flexural Modulus – ASTM D790 PSI 529300 690700 1418300 3084300 1443400 Flexural Strength – ASTM D790 PSI 23500 27300 36000 52100 30300 IMPACT Izod, Notched – ASTM D256 ft-lbs/in 1.0 0.7 1.1 1.3 0.6 Izod, Unnotched – ASTM D256 ft-lbs/in N.B. 13.1 15.3 13.8 5.0 THERMAL Melting Point – – °C 343 343 343 343 343 Glass Transition (DSC) – – °C 143 143 143 143 143 Heat Deflection Temp 264 psi, Unannealed ASTM D648 °C 151 178 320 325 > 300 CLTE, Flow Direction 23°C to 140°C ASTM E831 cm/cm/°C 4.0E-05 5.5E-05 2.2E-05 7.0E-06 1.9E-05 CLTE, Flow Direction 140°C to 250°C ASTM E831 cm/cm/°C 9.7E-05 7.8E-05 2.3E-05 6.5E-06 2.2E-05 Polyetheretherketone (PEEK) is widely considered to be one of the highest performing melt-processable polymers in the industry. You have the responsibility to conduct full-scale end-product performance testing to determine suitability in your application, and you assume all risk and liability arising from your use of the information and/or use or handling of any product. You have the responsibility to conduct full-scale end-product performance testing to determine suitability in your application, and you assume all risk and liability arising from your use of the information and/or use or handling of any product.

Stat-Tech Electrically Conductive Formulations for Pipette Tips Application Bulletin-CN Trilliant HC 导电方案 专为提升移液枪头精确性开发 ™ 应用公告 移液枪头的关键设计要素是精确地测量定量的液体。

Geon™ Bold vinyl solutions are dark, richly colored materials that stand up to the elements, especially heat build up, without losing their intensity or performance for windows, fencing, decking, and siding. Caption: This prototype heat sink for an LED ceiling light was molded in PVC from 3D printed inserts produced at the PolyOne Innovation Center in Avon Lake, Ohio.

P446 BROWN LOW HEAT BUILD P5 BROWN LOW HEAT BUILD

P5 BROWN LOW HEAT BUILD V3 P446 LOW HEAT BUILD V3

Externally heated manifolds are best. Internally heated systems, which use torpedo heaters, are not recommended because they have hot spots, stagnation zones and partially solidified material clinging to the walls.

The resin inherently offers heat resistance, but for some demanding applications, it also needs the addition of flame retardants to increase its resistance to flammability. Traditionally, these flame retardants have often contained polytetrafluoroethylene (PTFE), which is part of per- and polyfluorinated substances (PFAS), a group of chemicals widely used to resist heat, oil, stain, and water.

The material was found to be very slippery, resistant to high heat, and chemically inert. For example, the heat and chemical resistance of a fluoropolymer will greatly influence the pigment selection process.