Base Resin ABS PA PBT PC PE PEEK PP PPS Barrel Temperatures °F (°C) Rear Zone 400–475(200–250) 480–540 (248–282) 480–520 (250–270) 480–570 (250–300) 400–445 (200–230) 660–700 (350–475) 400–440 (200–225) 520–600 (270–300) Center Zone 410–480(205–253) 490–550 (254–287) 485–525 (251–273) 500–580 (260–305) 410–455 (207–237) 670–710 (357–385) 410–450 (205–230) 550–610 (285–310) Front Zone 420–490(210–257) 500–560 (260–293) 490–530 (254–276) 515–590 (267–310) 420–465 (213–243) 680–720 (363–400) 420–455 (215–235) 570–620 (300–320) Nozzle 425–500(215–260) 510–570 (265–298) 490–540 (254–282) 530–600 (275–315) 430–475 (220–250) 700–730 (370–395) 430–460 (220–240) 610–620 (320–325) Melt Temperature 425–515(215–270) 510–570 (265–298) 490–540 (254–282) 530–615 (275–325) 430–495 (220–260) 700–725 (370–385) 430–475 (220–250) 610–635 (320–335) Mold Temperature 140–200(60–90) 150–300 (65–148) 140–280 (60–137) 160–240 (70–115) 80–140 (25–60) 300–400 (150–200) 80–140 (25–60) 190–300 (90–150) Drying Parameters 190 (90) 2–4 Hours 0.01%–0.15% 180 (82) 4–5 Hours 0.10%–0.20% 275 (135) 3–4 Hours 0.02%–0.04% 250 (125) 3–4 Hours 0.02% 160 (70) 2 Hours 300 (150) 3–4 Hours 0.10% 160 (70) 2 Hours 280 (135) 2–3 Hours 0.01%–0.20% Nozzle Type General Purpose Nylon or Reverse Taper General Purpose General Purpose General Purpose General Purpose General Purpose General Purpose Injection Velocity1 2–5 in/sec; 50–127 mm/sec Injection Pressure Medium to high (may range from 1,000–4,000 psi; 7-28 Mpa) Back Pressure 50–100 psi; 0.3–0.7 Mpa Screw Speed 25–75 RPM Cushion 0.125–0.250 in; 3–6 mm Screw Compression Ratio2 2.0:1–2.5:1 Processing Guide 3 Base Resin ABS PA PBT PC PE PEEK PP PPS Barrel Temperatures °F (°C) Rear Zone 400–475(200–250) 480–540 (248–282) 480–520 (250–270) 480–570 (250–300) 400–445 (200–230) 660–700 (350–475) 400–440 (200–225) 520–600 (270–300) Center Zone 410–480(205–253) 490–550 (254–287) 485–525 (251–273) 500–580 (260–305) 410–455 (207–237) 670–710 (357–385) 410–450 (205–230) 550–610 (285–310) Front Zone 420–490(210–257) 500–560 (260–293) 490–530 (254–276) 515–590 (267–310) 420–465 (213–243) 680–720 (363–400) 420–455 (215–235) 570–620 (300–320) Nozzle 425–500(215–260) 510–570 (265–298) 490–540 (254–282) 530–600 (275–315) 430–475 (220–250) 700–730 (370–395) 430–460 (220–240) 610–620 (320–325) Melt Temperature 425–515(215–270) 510–570 (265–298) 490–540 (254–282) 530–615 (275–325) 430–495 (220–260) 700–725 (370–385) 430–475 (220–250) 610–635 (320–335) Mold Temperature 140–200(60–90) 150–300 (65–148) 140–280 (60–137) 160–240 (70–115) 80–140 (25–60) 300–400 (150–200) 80–140 (25–60) 190–300 (90–150) Drying Parameters 190 (90) 2–4 Hours 0.01%–0.15% 180 (82) 4–5 Hours 0.10%–0.20% 275 (135) 3–4 Hours 0.02%–0.04% 250 (125) 3–4 Hours 0.02% 160 (70) 2 Hours 300 (150) 3–4 Hours 0.10% 160 (70) 2 Hours 280 (135) 2–3 Hours 0.01%–0.20% Nozzle Type General Purpose Nylon or Reverse Taper General Purpose General Purpose General Purpose General Purpose General Purpose General Purpose Injection Velocity1 2–5 in/sec; 50–127 mm/sec Injection Pressure Medium to high (may range from 1,000–4,000 psi; 7-28 Mpa) Back Pressure 50–100 psi; 0.3–0.7 Mpa Screw Speed 25–75 RPM Cushion 0.125–0.250 in; 3–6 mm Screw Compression Ratio2 2.0:1–2.5:1 Comments 1. Only naturally balanced runner systems (“H” pattern) are recommended. 3.

Each cradle brace is a two-foot long, rectangular bar with a “U” shape machined into each end for a metallic insert.

VERDE 2975 U TL BLUE AS 2 OPAQUE BLUE

62861SLNS ANSP-SOLID ROYAL BLUR 286 U METALLIC BLUE MM425 BLUE

030YE2022 YELLOW PVC U BLUE-TWISTED PEPPERMINT STAN-TONE 42SP02 BLUE

PX-V-187(A) 2935 U BLU M3103 BASE TRANSL BLUE BLUE

5725 BLUE 9D-33831-06 BLUE PEARL AS V3 8508 GY2794B-U GREY

SC-2762 U NATURAL MB3186 BLUE DISSECTION PAD 10066065 BLUE

F588 BLUE PMS 1505 U BRIGHT ORANGE BLUE V1

PPG CORPORATE BLUE 5415UGNSPL PANTONE(R) 5415 U SIMULATION FLUORESCENT BLUE