Our high fiber volume, glass-reinforced thermoplastic panels and continuous resin transfer molding (CRTM) thermoset sandwich panels can streamline production and reduce system costs by eliminating assembly steps such as welding, drilling, bolting and riveting. Because the manufacturing process is continuous, it also provides significant cost savings over traditional composite panel manufacturing techniques. Our composite panels are custom engineered by varying core thicknesses to increase or decrease stiffness; by varying core materials (including end-grain balsa, foam or engineered woods) to increase or decrease weight; by varying fiber to modify the stiffness-to-weight ratio; and by varying the base polymer to increase or decrease strength. * 4 point flex., 44 in. span, ASTM 7249 Note: Additional core materials available.

Advanced Composites Explained LFT Basics - Understanding Long Fiber Thermoplastics Fiber-Line™ Specialty Engineered Thermoplastic Tapes

and will continue to serve on the  Board.  Ashish's appointment reinforces the Board's confidence in his leadership to generate long-term value creation for Our expanding portfolio of offerings includes colorants, advanced composites, functional additives, engineered materials, and Dyneema®, the world's strongest fiber™.

OnForce™ Long Glass Fiber Reinforced Thermoplastics: developed for automotive foot pedals, providing high dimensional stability, rigidity and flexibility, cyclic fatigue strength, and long-term creep resistance as well as excellent chemical and UV resistance, shows good colorability (including silver) and ease of processing Dyneema®, the world’s strongest fiber™, enables unmatched levels of performance and protection for end-use applications, including ballistic personal protection, marine and sustainable infrastructure and outdoor sports Sustainable infrastructure solutions that increase energy efficiency, renewable energy, natural resource conservation and fiber optic / 5G network accessibility  

Completes specialty acquisitions of Gordon Composites and Polystrand and establishes Advanced Composites platform Yesterday, the company announced the acquisitions of Gordon Composites and Polystrand, two specialty businesses that will join Polystrand establishes us with an immediate leadership position in new, next generation thermoplastic composites that combine high strength characteristics of a thermoset with the design freedom of thermoplastics."

LONG FIBER TECHNOLOGIES Complēt™ Long Fiber Reinforced Structural Thermoplastics OnForce™ Long Glass Fiber Reinforced Polypropylene Composites BE STRONGER, GET TOUGHER, GO LIGHTER Optimize stiffness, strength, and toughness to obtain structural performance with lightweight long fiber reinforced thermoplastics. Complēt™ long fiber reinforced structural thermoplastics and OnForce™ long glass fiber reinforced polypropylene composites utilize carbon, glass, or specialty fibers in a broad range of thermoplastic polymers to optimize material performance to your application requirements. Short glass fiber Injection molded part Long glass fiber CAPABILITIES TO BUILD BETTER Long fiber reinforced composite materials incorporate longer filaments of fiber reinforcement to increase mechanical properties and structural capabilities to higher levels than short fiber formulations.

POLYSTRAND CONTINUOUS FIBER REINFORCED THERMOPLASTIC TAPES & LAMINATES ™ PRODUCT SELECTION GUIDE Material Min Finished Slit Width Max Finished Slit Width Unidirectional Tape 2” (50.8 mm) 24” (610 mm) X-Ply™, 3-Ply, 4-Ply 2” (50.8 mm) 120” (3048 mm) SLITTING CAPABILITIES Max Unfinished Width Max Finished Slit Width Max Finished Roll Weight Max Roll Length (X-Ply™, Full Width) Up to 125" (3175 mm) Up to 120" (3048 mm) Up to 10,000 lbs (4500 kg) Up to 4,000 ft (1200 m) LAMINATION LINE CAPABILITIES Tape Width Resin Capabilities Fiber Inputs Max Tape Roll Weight Max Roll Length 25" (635 mm) Standard Width, Slit Capabilities PP, PE, PETG, aPET, PA6 Additional polymers in development E-Glass S-Glass, Aramid Up to 1,800 lbs (816 kg) Up to 12,000 ft (366 m) TAPE LINE CAPABILITIES Product Name Resin Fiber Content Areal Weight Nominal Thickness1 Flexural Modulus ASTM D790 Flexural Strength ASTM D790 Tensile Modulus ASTM D3039 Tensile Strength ASTM D3039 wt % lb/ft2 oz/yd2 gsm in mm ksi GPa ksi MPa ksi GPa ksi MPa 6337 PP 63 0.10 14.75 500 0.015 0.38 3570 24.6 58 402 4010 27.6 111 765 6531 65 0.05 7.40 251 0.006 0.15 4020 27.7 73 505 4900 33.8 140 965 6536 0.07 10.32 350 0.009 0.23 4050 27.9 72 494 4500 31.0 131 903 6538 0.14 19.77 670 0.019 0.48 3540 24.4 47 324 4260 29.4 100 689 7034B PP-Black 70 0.07 10.24 347 0.009 0.23 4400 30.3 83 569 5000 34.5 111 765 6020 PE 60 0.08 11.95 405 0.012 0.30 3600 24.8 54 372 3800 26.2 109 752 6621 66 0.10 13.97 474 0.012 0.30 4000 27.6 55 379 4720 32.5 126 869 68222 68 0.16 23.34 791 0.022 0.56 4060 28.0 55 379 4560 31.4 113 779 5843 PETG 58 0.08 11.85 402 0.008 0.20 3680 25.4 90 621 4400 30.3 137 945 5840B aPET-Black 58 0.09 13.00 441 0.009 0.23 4120 28.4 107 738 5080 35.0 150 1034 5860B PA6-Black 58 0.08 11.48 389 0.010 0.25 3620 25.0 104 717 3970 27.4 108 745 TYPICAL PROPERTIES - UNIDIRECTIONAL FIBERGLASS REINFORCED THERMOPLASTIC TAPE 1 Nominal thicknesses indicated are baseline values that may vary depending on material processing and other variables. TYPICAL PROPERTIES - MULTI-AXIAL LAMINATES 0° Testing Orientation 90° Testing Orientation Product Name Resin Fiber Content Laminate Layers & Orientation Areal Weight Nominal Thickness1 Flexural Modulus ASTM D790 Flexural Strength ASTM D790 Tensile Modulus ASTM D3039 Tensile Strength ASTM D3039 Flexural Modulus ASTM D790 Flexural Strength ASTM D790 Tensile Modulus ASTM D3039 Tensile Strength ASTM D3039 wt % lb/ft2 oz/yd2 gsm in mm ksi GPa ksi MPa ksi GPa ksi MPa ksi GPa ksi MPa ksi GPa ksi MPa 6337 PP 63 0/90 0.20 29.49 1000 0.031 0.79 - - - - 2020 13.9 59.7 412 - - - - 2020 13.9 59.7 412 0/90/0 0.31 44.24 1500 0.045 1.14 2250 15.5 46.4 320 3070 21.2 79.4 547 186 1.3 9.7 67 1330 9.2 39.6 273 0/90/90/0 0.41 58.98 2000 0.057 1.45 2000 13.8 44.0 303 2400 16.5 60.6 418 496 3.4 20.7 143 2210 15.2 56.4 389 6531 65 0/90 0.10 14.80 502 0.014 0.36 - - - - 2240 15.4 60.9 420 - - - - 2240 15.4 60.9 420 0/90/0 0.15 22.20 753 0.020 0.50 2650 18.3 58.3 402 3100 21.4 82.8 571 280 1.9 NB2 NB2 1670 11.5 42.5 293 0/90/90/0 0.21 29.61 1004 0.027 0.68 2260 15.6 51.5 355 2470 17.0 62.2 429 580 4.0 30.4 210 2310 15.9 59.6 411 6536 0/90 0.14 20.71 702 0.021 0.53 - - - - 1980 13.7 60.5 417 - - - - 1980 13.7 60.5 417 0/90/0 0.22 31.06 1053 0.029 0.74 2309 15.9 48.3 333 2730 18.8 81.5 562 245 1.7 13.0 90 1490 10.3 44.3 305 0/90/90/0 0.29 41.41 1404 0.037 0.94 2164 14.9 47 324 2170 15.0 59.6 411 512 3.5 25.4 175 2340 16.1 71.2 491 6538 0/90 0.27 39.54 1341 0.034 0.86 - - - - 2220 15.3 60.0 414 - - - - 2220 15.3 60.0 414 0/90/0 0.41 59.53 2018 0.057 1.44 2825 19.5 40.9 282 2780 19.2 67.6 466 218 1.5 10.2 70 1410 9.7 40.0 276 0/90/90/0 0.55 79.37 2691 0.073 1.85 1880 13.0 32.4 223 2060 14.2 54.0 372 478 3.3 18.0 124 2360 16.3 61.0 421 7034B PP-Black 70 0/90 0.14 20.48 694 0.016 0.40 - - - - 2680 18.5 62.0 427 - - - - 2680 18.5 62.0 427 0/90/0 0.21 30.72 1041 0.028 0.71 1750 12.1 55.9 385 3710 25.6 75.1 518 160 1.1 11.3 78 1440 9.9 36.2 250 0/90/90/0 0.28 40.95 1388 0.036 0.90 1700 11.7 40.4 279 2800 19.3 55.7 384 432 3.0 25.4 175 2350 16.2 52.4 361 6020 PE 60 0/90 0.17 23.90 810 0.023 0.57 - - - - 1830 12.6 52.00 359 - - - - 1830 12.6 52.0 359 0/90/0 0.25 35.86 1216 0.033 0.84 2265 15.6 40.0 276 2740 18.9 68.2 470 181 1.2 10.0 69 1350 9.3 35.3 243 0/90/90/0 0.33 47.81 1621 0.044 1.12 1810 12.5 30.0 207 2000 13.8 48.0 331 502 3.5 22.0 152 1820 12.5 46.0 317 6621 66 0/90 0.19 27.94 947 0.025 0.65 - - - - 2280 15.7 60.0 414 - - - - 2280 15.7 60.0 414 0/90/0 0.29 41.90 1421 0.040 1.01 2490 17.2 37.0 255 2900 20.0 70.0 483 165 1.1 9.7 67 1440 9.9 38.0 262 0/90/90/0 0.39 55.87 1894 0.053 1.35 1810 12.5 29.0 200 2160 14.9 58.0 400 508 3.5 21.0 145 2170 15.0 53.0 365 5843 PETG 58 0/90 0.16 23.70 804 0.020 0.50 - - - - 2050 14.1 59.6 411 - - - - 2050 14.1 59.6 411 0/90/0 0.25 35.55 1205 0.030 0.76 2800 19.3 89.0 614 2900 20.0 78.0 538 397 2.7 NB2 NB2 1580 10.9 42.5 293 0/90/90/0 0.33 47.40 1607 0.039 0.99 2540 17.5 72.0 496 2300 15.9 57.7 398 780 5.4 35.0 241 2170 15.0 63.0 434 5840B aPET-Black 58 0/90 0.18 26.01 882 0.021 0.53 - - - - 2530 17.4 55.3 381 - - - - 2530 17.4 55.3 381 0/90/0 0.27 39.01 1323 0.032 0.82 2986 20.6 91.1 628 3160 21.8 68.7 474 252 1.7 20.0 138 1580 10.9 36.9 254 0/90/90/0 0.36 52.01 1763 0.042 1.07 3065 21.1 73.1 504 2570 17.7 54.2 374 813 5.6 37.0 255 2440 16.8 55.6 383 5860B PA6-Black 58 0/90 0.16 22.95 778 0.021 0.52 - - - - 2190 15.1 56.00 386 - - - - 2190 15.1 56.0 386 0/90/0 0.24 34.43 1167 0.034 0.86 2510 17.3 117.0 807 2760 19.0 63.7 439 657 4.5 22.2 153 1630 11.2 39.7 274 0/90/90/0 0.32 45.91 1556 0.046 1.18 2210 15.2 106.0 731 2090 14.4 45.6 314 1110 7.7 50.8 350 2150 14.8 57.4 396 1 Nominal thicknesses indicated are baseline values that may vary depending on material processing and other variables.

Continuous Glucose Monitors (CGM) Advanced Mobility Composite Structures Thermoplastic Elastomers

The consensus was clear: the world’s strongest fiber™ just got stronger. This innovation pushes fabric engineering to new heights, delivering a composite that can withstand some of the most extreme and demanding environments, reinforcing Dyneema® as the global leader in fiber technology. Our expanding portfolio of offerings includes colorants, advanced composites, functional additives, engineered materials, and Dyneema®, the world’s strongest fiber™.

THICKNESS (in)* RESIN FLEXURAL STRENGTH (x10^3 psi) FLEXURAL MODULUS (x10^6 psi) STRAIN (%) FIBER CONTENT (wt%) MIN Vinyl Ester 115 4.0 3.3 68 AVG Vinyl Ester 124 4.6 3.2 71 MIN Epoxy 138 5.1 2.3 65 AVG Epoxy 153 5.5 2.3 67 Avient’s composite springs are manufactured using a continuous pultrusion process. Resin impregnated, continuous glass fibers are drawn through a curing die of a specific cross section, yielding consistent quality, dimensions and mechanical properties to provide more consistent spring rates than alternate materials. Reinforcement fiber configurations are designed to provide high flexural strength and modulus in the axial direction plus fastener bearing strength in the transverse direction. * Flexural properties are dependent on thickness.