AUTOMOTIVE OEM C E N T R A L C O N S O L E P A R T • Metallic aspect • Good surface appearance • UV resistance • Cost effective alternative to paint • Offered a paint replacement solution with a molded-in-color metallic effect • Provided color matching expertise • Utilized simulation tools to predict part aspect and suggest the best injection point for process and mold optimization • Optimized formulation for metallic effects Smartbatch Combination Colorants & Additives KEY REQUIREMENTS WHY AVIENT?

AUTOMOTIVE OEM C E N T R A L C O N S O L E P A R T • Metallic aspect • Good surface appearance • UV resistance • Cost effective alternative to paint • Offered a paint replacement solution with a molded-in-color metallic effect • Provided color matching expertise • Utilized simulation tools to predict part aspect and suggest the best injection point for process and mold optimization • Optimized formulation for metallic effects Smartbatch™ Combination Colorants & Additives KEY REQUIREMENTS WHY AVIENT?

% Pigment Specific Gravity Color Index Lightfastness WHITE 10PEP03 Titanium Dioxide, Rutile 60 2.06 PW-6 I/O YELLOW 12PEP01 Diarylide AAOT GS 20 1.24 PY-14 I 12PEP03 Diarylide HR RS 25 1.23 PY-83 I/O (Mass) 13PEP02 Isoindolinone RS 25 1.31 PY-110 I/O 13PEP03 Benzimidazolone GS 25 1.25 PY-151 I/O (Mass) 81PEP01 Iron Oxide 60 2.07 PY-42 I/O ORANGE 15PEP03 Benzimidazolone RS 25 1.27 PO-36 I/O RED 23PEP04 Quinacridone BS 25 1.24 PV-19 I/O 23PEP06 Specialty Naphthol BS 25 1.23 PR-170 I/O (Mass) C 25PEP01 Red 2B, Ca Salt BS 17 1.26 PR-48:2 I/O (Mass) 28PEP01 Red 2B, Ba Salt YS 25 1.32 PR48:1 I/O (Mass) 82PEP01 Iron Oxide, Light YS 27 1.5 PR-101 I/O 82PEP02 Iron Oxide, Light BS 60 2.2 PR-101 I/O 82PEP04 Iron Oxide, Light VYS 60 2.2 PR-101 I/O 82PEP05 Iron Oxide, Dark VBS 60 2.21 PR-101 I/O BLUE 40PEP01 Phthalocyanine GS 25 1.27 PB-15:3 I/O 40PEP05 Phthalocyanine RS 25 1.27 PB-15 I/O 42PEP02 Ultramarine 35 1.44 PB-29 I/O 49PEP01 Cobalt 31 1.54 PB-28 I/O GREEN 50PEP01 Phthalocyanine BS 16 1.28 PG-7 I/O 50PEP03 Phthalocyanine YS 16 1.28 PG-7 I/O 59PEP02 Chromium Oxide 70 2.6 PG-17 I/O VIOLET/MAGENTA 24PEP03 Quinacridone Violet 20 1.24 PV-19 I/O 24PEP04 Ultramarine Violet 50 1.69 PV-15 I/O 24PEP05 Quinacridone Magenta 20 1.24 PR-122 I/O 24PEP06 Benzimidazolone 20 1.23 PV-32 I/O 24PEP07 Carbazole Violet 13 1.22 PV-23 I/O BROWN/TAN 83PEP01 Iron Oxide, Light 34 1.6 PBr-6 I/O 83PEP02 Iron Oxide, Dark 29 1.51 PBr-6 I/O BLACK 90PEP01 Furnace - High Jet 24 1.3 PBk-7 I/O 90PEP04 Furnace - Medium 17 1.27 PBk-7 I/O 90PEP05 Iron Oxide 33 1.58 PBk-11 I/O POLYESTER URETHANE PASTE COLORANTS (PEP) Stan-Tone Code Pigment Type Approx. % Pigment Specific Gravity Color Index Lightfastness WHITE 10ET03 Titanium Dioxide, Rutile 56 1.74 PW-6 I/O YELLOW 12ET01 Diarylide AAOT GS 40 1.15 PY-14 I 12ET03 Diarylide HR RS 20 1.07 PY-83 I/O (Mass) 13ET02 Isoindolinone RS 20 1.11 PY-110 I/O 13ET03 Benzimidazolone GS 20 1.08 PY-151 I/O (Mass) 81ET01 Iron Oxide 60 1.84 PY-42 I/O ORANGE 15ET03 Benzimidazolone RS 25 1.11 PO-36 I/O RED 20ET01 Red Lake C YS 30 1.16 PR-53 I 22ET01 Lithol Rubine BS 30 1.17 PR-57:1 I 23ET04 Quinacridone BS 15 1.05 PV-19 I/O 23ET06 Specialty Naphthol BS 30 1.09 PR-170 I/O (Mass) C 25ET01 Red 2B, Ca Salt BS 29 1.15 PR-48:2 I/O (Mass) 28ET01 Red 2B, Ba Salt YS 30 1.18 PR-48:1 I/O (Mass) 82ET01 Iron Oxide, Light BS 60 1.94 PR-101 I/O 82ET02 Iron Oxide, Dark VBS 60 1.95 PR-101 I/O 82ET04 Iron Oxide, Light VYS 60 1.94 PR-101 I/O BLUE 40ET01 Phthalocyanine GS 25 1.11 PB-15:3 I/O 40ET05 Phthalocyanine RS 20 1.09 PB-15 I/O 42ET02 Ultramarine 55 1.46 PB-29 I/O 49ET01 Cobalt 65 2.02 PB-28 I/O GREEN 50ET01 Phthalocyanine BS 30 1.2 PG-7 I/O 50ET03 Phthalocyanine YS 25 1.16 PG-7 I/O 59ET01 Chromium Oxide 65 2.12 PG-17 I/O VIOLET/MAGENTA 24ET03 Quinacridone Violet 20 1.08 PV-19 I/O 24ET04 Ultramarine Violet 60 1.66 PV-15 I/O 24ET05 Quinacridone Magenta 20 1.08 PR-122 I/O 24ET06 Benzimidazolone 25 1.08 PV-32 I/O 24ET07 Carbazole Violet 13 1.05 PV-23 I/O BROWN/TAN 83ET01 Iron Oxide, Light 64 2.02 PBr-6 I/O 83ET02 Iron Oxide, Dark 60 1.9 PBr-6 I/O BLACK 90ET04 Furnace - Medium 22 1.12 PBk-7 I/O 90ET05 Iron Oxide 60 1.9 PBk-11 I/O POLYETHER URETHANE PASTE COLORANTS (ET) PEP/ET RS = Red Shade YS = Yellow Shade VYS = Very Yellow Shade BS = Blue Shade VBS = Very Blue Shade GS = Green Shade HR = Heat-Resistant LIGHTFASTNESS I = Indoor Only I/O = Indoor or Outdoor Mass = Outdoor Masstone Application Only C = Some Caution Advised www.avient.com Copyright © 2020, Avient Corporation.

Required Must be signed by all incorporators, if amended by incorporators, or an authorized officer if amended by directors or shareholders, pursuant to Ohio Revised Code section 1701.73(B) and (C). James S T A T E OF O H I O C E R T I F I C A T E Ohio Secretary of State, Frank LaRose 4463782 It is hereby certified that the Secretary of State of Ohio has custody of the business records for and, that said business records show the filing and recording of: AVIENT CORPORATION United States of America State of Ohio Office of the Secretary of State Witness my hand and the seal of the Secretary of State at Columbus, Ohio this 23rd day of April, A.D. 2020. Ohio Secretary of State 202011402526NAME RESERVATION Document(s) Document No(s): C T CORPORATION SYSTEM 4400 EASTON COMMONS WAY SUITE 125 COLUMBUS, OH 43219 This is not a bill.

TEMPERATURE, MPa Temperature (C) S tr en gt h (M M od ul us (G FLEXURAL MODULUS VS. TEMPERATURE, GPa Temperature (C) FLEXURAL FATIGUE STRENGTH, MPa Cycles to Failure (in thousands) F at iq ue S tr en gt h (M INSTALLATION INSTRUCTIONS Proper installation of composite springs from Avient is essential to achieve optimal performance and maximum service life. Exposure to finishing operations: One time exposure to elevated temperatures of up to 400°F (204°C) for 15 to 20 minutes, typical for the application of coatings, have no effect on the performance of the composite springs.

°C 425-480 Property UOM Value Breaking Tenacity g/d 23.0 Specific Gravity Ratio 1.44 Elongation @ Break % 3.5 Tensile Modulus g/d 555 Moisture Regain* % 5.0 Creep** % °C 425-480 Standard Modulus High Modulus CHEMICAL COMPATIBILITY Chemical Resistance to Acid: Degrades in Formic, Hydrochloric, and Sodium Hydroxide acid. KEVLAR® PARA-ARAMID DATA KEVLAR® PARA-ARAMID (HM) BARE FIBER PERFORMANCE * Equilibrium moisture regain @ 55% RH ** Creep @ 40%-58% ultimate tensile strength *** Shrinkage in dry air @ 177 C for 30 minutes ABOUT FIBER-LINE® LOCATIONS Headquarters, R&D, Manufacturing FIBER-LINE® LLC 3050 Campus Drive Hatfield, PA 19440 +1 215.997.9181 fiber@fiber-line.com Manufacturing Operations FIBER-LINE® LLC 280 Performance Drive SE Hickory, NC 28602 +1 828.326.8700 fiber@fiber-line.com EMEA & Asia Pacific Operations FIBER-LINE® INTERNATIONAL B.V.

16550 EPIC RIVAL SPORT VICTORY ANTHRA-C

c/o

Formulated for consumer and transportation markets, these grades can be used in applications such as personal care products, automotive interior and under-the-hood components, lawn and garden tools, outdoor goods, office supplies, USB-C cables, footwear and houseware durables. 

Bradley C.