glass, carbon, etc.) • Fiber reinforcement percentage (ranging from 20–70% fiber content, by weight) • Additive technologies (color, UV enhancement, flame retardancy, heat stabilization, etc.)

They process easily across all standard fiber loading ranges of long glass, long carbon, or hybrid combinations of fiber.

Overview • FIBER-LINE® extrusion is the process of forming a polymer jacket of various thickness around a core of high-performance fibers • Fiber core can be parallel, twisted, or in rope form • Polymer jacket selected to optimize flex, chemical, temperature, & UV resistance Key Features • .50mm – 30.00mm size capability • Protect the core from mechanical, environmental, and chemical damage • Extend life of cable or strength member • Enhance flame & chemical resistance • Improve UV resistance • Many polymers available FIBER-LINE® FIBERS SUITABLE FOR EXTRUSION • Kevlar® Para-Aramid • Vectran® LCP • Zylon® PBO • Technora® • Carbon Fiber • Fiberglass FIBER-LINE® PRODUCTS ADDED BY EXTRUSION • Strength members • Tracer-wire • Micro-cable • Ruggedized cable Our Polymer Offering • EPC • ETFE • FEP • Hytrel • PFA • Polyethylene • Polypropylene • Polyurethane • PVC • PVDF EXTRUSION FIBERS PROCESSES PRODUCTS FIBER OPTICAL CABLES MOVING HIGH PERFORMANCE FIBERS FORWARD This data is provided for informational purposes only, and does not constitute a specification.

Monolayer PET is one of the lightest weight packaging options reducing raw material requirements and carbon emissions during transportation.

At the recommended use levels in CSD (carbonated soft drinks) applications (around 5ppm), the blue toner is not required and a reduced amount of the red toner may be desirable (in some cases red toner can also be eliminated; this depends on the inherent color of the resin and so cannot be specified here). • Other additives, such as Phosphoric Acid (which is typically used as a thermal stabilizer) can be used in conjunction with Joule RHB additive and may be dosed at the same point if process constraints dictate, but only when using a separate lance to that used for the reheat additive.

glass or carbon) that are in parallel alignment and of uniform length (typically 12 mm), offering metal replacement performance.

CAPS & CLOSURES INDUSTRY BULLETIN FOOD & BEVERAGE Requirements: Ensure product containment, prevent leaks, and withstand pressure, especially in carbonated drinks.

GL AS S/ EP OX Y TA B M AT ER IA L N O T AB BOTTOM PANEL LEG LENGTH BREAK STRENGTH Hammerhead with 5 lb/ft3 (80 kg/m3) Core Density 2 in 51 mm 420 lbs 191 kg Hammerhead with 7 lb/ft3 (115 kg/m3) Core Density 2 in 51 mm 370 lbs 168 kg Hammerhead with 8 lb/ft3 (135 kg/m3) Core Density 2 in 51 mm 332 lbs 151 kg Marine Plywood 2 in 51 mm 984 lbs 446 kg Glass/Polyester with Balsa Core 2 in 51 mm 1298 lbs 589 kg Hammerhead with 5 lb/ft3 (80 kg/m3) Core Density - ITW Plexus MA420 Adhesive NA 501 lbs 227 kg Hammerhead with 7 lb/ft3 (115 kg/m3) Core Density - ITW Plexus MA420 Adhesive NA 839 lbs 381 kg Hammerhead with 8 lb/ft3 (135 kg/m3) Core Density - ITW Plexus MA420 Adhesive NA 1156 lbs 524 kg Hammerhead with 8 lb/ft3 (135 kg/m3) Core Density - Crestomer 1152PA Adhesive NA 1530 lbs 694 kg Hammerhead with 8 lb/in3 (135 kg/m3) Core Density - Crestomer M1-30 Adhesive NA 1471 lbs 667 kg Mixed Conditions ADHESIVE DESCRIPTION ADHESIVE GRADE MANUFACTURER AVERAGE BOND STRENGTH STANDARD DEVIATION FAILURE MODE BEST ADHESION 2k Urethane 75421 Lord 2281 psi 15.73 MPa 184 psi 1.27 MPa Substrate Cohesive 2k Acrylic SA1-705 GRY1 AccraLock 2211 psi 15.24 MPa 78 psi 0.54 MPa Substrate 2k Acrylic Plexus MA420 ITW 2171 psi 14.97 MPa 262 psi 1.81 MPa Substrate 2k Acrylic SA10-05 Blk1 AccraLock 2102 psi 14.49 MPa 138 psi 0.95 MPa Substrate 2k Urethane 75451 Lord 2047 psi 14.11 MPa 68 psi 0.47 MPa Cohesive 2k Acrylic SA1-705 GRY 1:2 AccraLock 1966 psi 13.56 MPa 68 psi 0.47 MPa Substrate 2k Acrylic Scotchweld 8010 3M 1907 psi 13.15 MPa 61 psi 0.42 MPa Adhesive Cyanoacrylate Gorilla Glue Gorilla Glue 1885 psi 13.00 MPa 432 psi 2.98 MPa Cohesive 2k Acrylic Crestabond PP-04 Scott Bader 1873 psi 12.91 MPa 281 psi 1.94 MPa Substrate 2k Acrylic SA10-05 Blk 10:2 AccraLock 1779 psi 12.27 MPa 127 psi 0.88 MPa Cohesive 2k Urethane 75422 Lord 1716 psi 11.83 MPa 190 psi 1.31 MPa Cohesive Adhesive 2k Urethane 75452 Lord 1535 psi 10.58 MPa 98 psi 0.68 MPa Adhesive 2k Methacrylate Polyfuse Icon Containment 1610 psi 11.10 MPa 98 psi 0.68 MPa Adhesive INTERMEDIATE ADHESION 2k Acrylic FA10-05 Blk C010817 AccraLock 724 psi 4.99 MPa 58 psi 0.40 MPa Cohesive 2k Acrylic FA10-05 Blk1 AccraLock 722 psi 4.98 MPa 44 psi 0.30 MPa Cohesive 2k Epoxy Loctite Epoxy Instant Mix Loctite 508 psi 3.50 MPa 81 psi 0.56 MPa Adhesive 2k Epoxy Gorilla Glue Epoxy Gorilla Glue 341 psi 2.35 MPa 198 psi 1.37 MPa Adhesive NOT RECOMMENDED 2k Epoxy Loctite Epoxy Marine Loctite 0 0 No bond ADHESIVE SELECTION Brands identified are owned by the manufacturers of the adhesive products. 1 surface sanded with 220 grit scuff prep 2 surface primed with 459T FASTENER TYPE BENEFITS CONSIDERATIONS Through-Bolting Best mechanical locking system Need back side access to panel Screw-In Anchor Highest pullout strength Requires pilot hole Cup Washer Spreads compressive load Requires relief hole; For substructure and hard point attachment Wide Grip (Bulb-Style) Rivet Ease of use—no installation torque limitations For lower load attachments Sheet Metal or Wood Screw Readily available, low cost Penetrate both skins for improved pullout Shoulder Washer Limits compressive load Requires relief hole; For substructure and hard point attachment For more information on installation, adhesives, and fasteners for specific applications, please contact Avient.

Wall Thickness (mm) C o o li n g T im e ( S e c ) 40 35 30 25 20 15 10 5 0 0 1 2 3 4 ABS PC Nylon 6/6 FIGURE 1 - Wall thickness vs. cooling time of various plastics FIGURE 2 - Designing for wall thickness changes FIGURE 3 - Internal and external radius guidelines FIGURE 4 - Coring for tight radius design ESCR Design Guide 2 CONTOUR Where possible, contouring the products’ exterior form, as shown in Figure 5, can help to eliminate pooling of fluids.

GL AS S/ EP OX Y TA B M AT ER IA L N O T AB BOTTOM PANEL LEG LENGTH BREAK STRENGTH Hammerhead with 5 lb/ft3 (80 kg/m3) Core Density 2 in 51 mm 420 lbs 191 kg Hammerhead with 7 lb/ft3 (115 kg/m3) Core Density 2 in 51 mm 370 lbs 168 kg Hammerhead with 8 lb/ft3 (135 kg/m3) Core Density 2 in 51 mm 332 lbs 151 kg Marine Plywood 2 in 51 mm 984 lbs 446 kg Glass/Polyester with Balsa Core 2 in 51 mm 1298 lbs 589 kg Hammerhead with 5 lb/ft3 (80 kg/m3) Core Density - ITW Plexus MA420 Adhesive NA 501 lbs 227 kg Hammerhead with 7 lb/ft3 (115 kg/m3) Core Density - ITW Plexus MA420 Adhesive NA 839 lbs 381 kg Hammerhead with 8 lb/ft3 (135 kg/m3) Core Density - ITW Plexus MA420 Adhesive NA 1156 lbs 524 kg Hammerhead with 8 lb/ft3 (135 kg/m3) Core Density - Crestomer 1152PA Adhesive NA 1530 lbs 694 kg Hammerhead with 8 lb/in3 (135 kg/m3) Core Density - Crestomer M1-30 Adhesive NA 1471 lbs 667 kg Mixed Conditions ADHESIVE DESCRIPTION ADHESIVE GRADE MANUFACTURER AVERAGE BOND STRENGTH STANDARD DEVIATION FAILURE MODE BEST ADHESION 2k Urethane 75421 LORD 2281 psi 15.73 MPa 184 psi 1.27 MPa Substrate Cohesive 2k Acrylic SA1-705 GRY1 ACRALOCK 2211 psi 15.24 MPa 78 psi 0.54 MPa Substrate 2k Acrylic Plexus MA420 ITW 2171 psi 14.97 MPa 262 psi 1.81 MPa Substrate 2k Acrylic SA10-05 Blk1 ACRALOCK 2102 psi 14.49 MPa 138 psi 0.95 MPa Substrate 2k Urethane 75451 LORD 2047 psi 14.11 MPa 68 psi 0.47 MPa Cohesive 2k Acrylic SA1-705 GRY 1:1 ACRALOCK 1966 psi 13.56 MPa 68 psi 0.47 MPa Substrate 2k Acrylic Scotch-Weld 8010 3M 1907 psi 13.15 MPa 61 psi 0.42 MPa Adhesive Cyanoacrylate Gorilla Glue Gorilla Glue 1885 psi 13.00 MPa 432 psi 2.98 MPa Cohesive 2k Acrylic Crestabond PP-04 Scott Bader 1873 psi 12.91 MPa 281 psi 1.94 MPa Substrate 2k Acrylic SA10-05 Blk 10:1 ACRALOCK 1779 psi 12.27 MPa 127 psi 0.88 MPa Cohesive 2k Urethane 75422 LORD 1716 psi 11.83 MPa 190 psi 1.31 MPa Cohesive Adhesive 2k Urethane 75452 LORD 1535 psi 10.58 MPa 98 psi 0.68 MPa Adhesive 2k Methacrylate PolyFuse Icon Containment 1610 psi 11.10 MPa 98 psi 0.68 MPa Adhesive INTERMEDIATE ADHESION 2k Acrylic FA10-05 Blk C010817 ACRALOCK 724 psi 4.99 MPa 58 psi 0.40 MPa Cohesive 2k Acrylic FA10-05 Blk1 ACRALOCK 722 psi 4.98 MPa 44 psi 0.30 MPa Cohesive 2k Epoxy Loctite Epoxy Instant Mix Loctite 508 psi 3.50 MPa 81 psi 0.56 MPa Adhesive 2k Epoxy Gorilla Epoxy Gorilla Glue 341 psi 2.35 MPa 198 psi 1.37 MPa Adhesive NOT RECOMMENDED 2k Epoxy Loctite Epoxy Marine Loctite 0 0 No bond ADHESIVE SELECTION Brand names of the adhesives are owned by the respective manufacturers.