Consequentially many brand owners are already looking to reduce the inorganic content in their packaging to TECHNOLOGY BENEFITS • Improved light blocking performance up to 99.9% at 550nm and 700nm • Brighter whiteness L* >90 even in thin wall sections (0.21mm) • Plug & go solution—processes similar to virgin PET • Process with standard PET grades and rPET • Reduces equipment wear and tear • TiO2 content of This literature shall NOT operate as permission, recommendation, or inducement to practice any patented invention without permission of the patent owner. 1.844.4AVIENT www.avient.com PROPERTIES LACTRA™ FOUR LACTRA™ ONE LACTRA™ ZERO TiO2 % in bottles at UHT LDR 3% 1% 0% Recommended LDR for UHT 10% 7% 10% Light blocking at 550nm at UHT LDR >99.9% >99.8% >99.9% Light blocking at 700nm at UHT LDR >99.9% >99.8% >99.9% Color L* >90 >88 >90 COLORMATRIX LACTRA LOW-TIO2 RANGE

% Pigment Specific Gravity Color Index Lightfastness WHITE 10PEP03 Titanium Dioxide, Rutile 60 2.06 PW-6 I/O YELLOW 12PEP01 Diarylide AAOT GS 20 1.24 PY-14 I 12PEP03 Diarylide HR RS 25 1.23 PY-83 I/O (Mass) 13PEP02 Isoindolinone RS 25 1.31 PY-110 I/O 13PEP03 Benzimidazolone GS 25 1.25 PY-151 I/O (Mass) 81PEP01 Iron Oxide 60 2.07 PY-42 I/O ORANGE 15PEP03 Benzimidazolone RS 25 1.27 PO-36 I/O RED 23PEP04 Quinacridone BS 25 1.24 PV-19 I/O 23PEP06 Specialty Naphthol BS 25 1.23 PR-170 I/O (Mass) C 25PEP01 Red 2B, Ca Salt BS 17 1.26 PR-48:2 I/O (Mass) 28PEP01 Red 2B, Ba Salt YS 25 1.32 PR48:1 I/O (Mass) 82PEP01 Iron Oxide, Light YS 27 1.5 PR-101 I/O 82PEP02 Iron Oxide, Light BS 60 2.2 PR-101 I/O 82PEP04 Iron Oxide, Light VYS 60 2.2 PR-101 I/O 82PEP05 Iron Oxide, Dark VBS 60 2.21 PR-101 I/O BLUE 40PEP01 Phthalocyanine GS 25 1.27 PB-15:3 I/O 40PEP05 Phthalocyanine RS 25 1.27 PB-15 I/O 42PEP02 Ultramarine 35 1.44 PB-29 I/O 49PEP01 Cobalt 31 1.54 PB-28 I/O GREEN 50PEP01 Phthalocyanine BS 16 1.28 PG-7 I/O 50PEP03 Phthalocyanine YS 16 1.28 PG-7 I/O 59PEP02 Chromium Oxide 70 2.6 PG-17 I/O VIOLET/MAGENTA 24PEP03 Quinacridone Violet 20 1.24 PV-19 I/O 24PEP04 Ultramarine Violet 50 1.69 PV-15 I/O 24PEP05 Quinacridone Magenta 20 1.24 PR-122 I/O 24PEP06 Benzimidazolone 20 1.23 PV-32 I/O 24PEP07 Carbazole Violet 13 1.22 PV-23 I/O BROWN/TAN 83PEP01 Iron Oxide, Light 34 1.6 PBr-6 I/O 83PEP02 Iron Oxide, Dark 29 1.51 PBr-6 I/O BLACK 90PEP01 Furnace - High Jet 24 1.3 PBk-7 I/O 90PEP04 Furnace - Medium 17 1.27 PBk-7 I/O 90PEP05 Iron Oxide 33 1.58 PBk-11 I/O POLYESTER URETHANE PASTE COLORANTS (PEP) Stan-Tone Code Pigment Type Approx. % Pigment Specific Gravity Color Index Lightfastness WHITE 10ET03 Titanium Dioxide, Rutile 56 1.74 PW-6 I/O YELLOW 12ET01 Diarylide AAOT GS 40 1.15 PY-14 I 12ET03 Diarylide HR RS 20 1.07 PY-83 I/O (Mass) 13ET02 Isoindolinone RS 20 1.11 PY-110 I/O 13ET03 Benzimidazolone GS 20 1.08 PY-151 I/O (Mass) 81ET01 Iron Oxide 60 1.84 PY-42 I/O ORANGE 15ET03 Benzimidazolone RS 25 1.11 PO-36 I/O RED 20ET01 Red Lake C YS 30 1.16 PR-53 I 22ET01 Lithol Rubine BS 30 1.17 PR-57:1 I 23ET04 Quinacridone BS 15 1.05 PV-19 I/O 23ET06 Specialty Naphthol BS 30 1.09 PR-170 I/O (Mass) C 25ET01 Red 2B, Ca Salt BS 29 1.15 PR-48:2 I/O (Mass) 28ET01 Red 2B, Ba Salt YS 30 1.18 PR-48:1 I/O (Mass) 82ET01 Iron Oxide, Light BS 60 1.94 PR-101 I/O 82ET02 Iron Oxide, Dark VBS 60 1.95 PR-101 I/O 82ET04 Iron Oxide, Light VYS 60 1.94 PR-101 I/O BLUE 40ET01 Phthalocyanine GS 25 1.11 PB-15:3 I/O 40ET05 Phthalocyanine RS 20 1.09 PB-15 I/O 42ET02 Ultramarine 55 1.46 PB-29 I/O 49ET01 Cobalt 65 2.02 PB-28 I/O GREEN 50ET01 Phthalocyanine BS 30 1.2 PG-7 I/O 50ET03 Phthalocyanine YS 25 1.16 PG-7 I/O 59ET01 Chromium Oxide 65 2.12 PG-17 I/O VIOLET/MAGENTA 24ET03 Quinacridone Violet 20 1.08 PV-19 I/O 24ET04 Ultramarine Violet 60 1.66 PV-15 I/O 24ET05 Quinacridone Magenta 20 1.08 PR-122 I/O 24ET06 Benzimidazolone 25 1.08 PV-32 I/O 24ET07 Carbazole Violet 13 1.05 PV-23 I/O BROWN/TAN 83ET01 Iron Oxide, Light 64 2.02 PBr-6 I/O 83ET02 Iron Oxide, Dark 60 1.9 PBr-6 I/O BLACK 90ET04 Furnace - Medium 22 1.12 PBk-7 I/O 90ET05 Iron Oxide 60 1.9 PBk-11 I/O POLYETHER URETHANE PASTE COLORANTS (ET) PEP/ET RS = Red Shade YS = Yellow Shade VYS = Very Yellow Shade BS = Blue Shade VBS = Very Blue Shade GS = Green Shade HR = Heat-Resistant LIGHTFASTNESS I = Indoor Only I/O = Indoor or Outdoor Mass = Outdoor Masstone Application Only C = Some Caution Advised www.avient.com Copyright © 2020, Avient Corporation.

INDUSTRY BULLETIN STANDARD UNITS ONFLEX LO 7120-45N Volatile Organic Compounds VDA 278 ug/g(ppm) 41 Fogging VDA 278 ug/g(ppm) 521 Odor • Control • Dry conditions • Wet conditions SAE J1351 (15) 1-10 Scale 1 2 1 Compression Set (23°C) • 22 hours • 70 hours ASTM D395 % 14.4 14.6 Capillary Viscosity • 1341/s • 11170/s ASTM D3835 Pa*s 35 7 HVAC SYSTEMS OnFlex™ LO • Features: low VOC/FOG, low odor, good compression set, easy processing, overmolds to polypropylene • Example applications: seals and flaps in heating, ventilation and air conditioning systems CHARACTERISTICS ONFLEX™ LO ONFLEX™ AF TPE GENERAL PURPOSE TPV TPO Volatile Organic Compounds (VDA 278) Very Low Moderate Moderate Moderate Very Low Fogging (VDA 278 & DIN 75201) Very Low Moderate Moderate High Very Low Odor (VDA 270 Requirement ≤3.0) ≤3.0 ≤3.0 >3 >3 ≤3.0 Gloss Level Low Low Low Very Low High Tactile Feel Grippy Grippy Grippy Grippy Waxy Pre-Drying Required No No No Yes No Raw Material Costs $$ $$ $$ $$$ $ Compression Set @ RT Good Good Good Excellent N/A Compression Set @ ≥70°C Moderate Moderate Moderate Good N/A UV Resistance Good Excellent Good Good Good Weatherability Good Excellent Good Good Good Hardness Range Low to High Low to High Low to High Low to High High Density (g/ml) 1.15 0.99 0.90–1.20 0.95–0.98 0.90–1.20 GENERAL CHARACTERISTICS COMPARING TPE, TPV, TPO Grades shown on both pages are representative of solutions manufactured in North America, more grades available globally.

Microsoft Word - Terms and Conditions Finland _8 April 2014_.doc TERMS AND CONDITIONS These Terms and Conditions apply to the sale of Products by PolyOne Corporation and its subsidiaries. 1. All late payments shall bear an annual interest of one (1) month EURIBOR plus 8% accrued on a daily basis, notwithstanding any damages. Seller may deliver to Buyer a quantity of Products with a quantity tolerance which may vary, depending upon the quantities ordered by Buyer, as follows: (1) from 50 to 99 kgs, +/- 25%; (2) from 100 to 249 kgs, +/- 15%; (3) from 250 to 499 kgs, +/- 10%; (4) more than 500 kgs, +/- 5%.

PP OVERMOLDING HARDNESS REGULATORY STERILIZATION CHARACTERISTICS Dynaflex™ G2706 28A USP Class VI, ISO 10993, Food contact EtO Soft translucent grade, grippy feel Dynaflex™ G2711 43A USP Class VI, ISO 10993, Food contact EtO Highly colorable solution, grippy feel, low compression set Versaflex™ CL2242 & CL2250 42A/ 50A USP Class VI, ISO 10993, US Food contact EtO Clear boilable grades; ABS, PC bondable Versaflex™ G2705 N 60A USP Class VI, ISO 10993, Food contact EtO/Steam High resilience, low compression set Versaflex™ HC3810 20A-90A USP Class VI, ISO 10993 EtO General purpose, unfilled ABS, PC OVERMOLDING HARDNESS REGULATORY STERILIZATION CHARACTERISTICS Versaflex™ OM1040 40A USP Class VI, ISO 10993 EtO Translucent Versaflex™ OM3060 60A USP Class VI, ISO 10993 EtO Clear VERSAFLEX™ CL AND DYNAFLEX™ TPEs OVERMOLDING FOR ERGONOMICS • Adds good tactile surface with soft-touch feel • Available in a variety of color effects and textures • Improves grip, cushion, and comfort • Enhances functional performance like sealing properties, vibration damping, oxygen barrier, and scratch and abrasion resistance • Reduces assembly costs, good processability • Offers excellent adhesion to a wide range of substrates • Glucometers • Medical tools overmolds • Injector pens • Analysis devices VERSALLOY™ HC & VERSAFLEX™ HC TPEs SEALING & RESEALING • Rubbery feel and soft touch • No coring, good puncture, and resealability in static stoppers • Meets low coefficient of friction requirements in dynamic seals • Low extractables • Suitable to overmold onto polyolefins • Sealing and resealing septum • Seals and sanitary gaskets • Syringe plungers and tips MATERIAL DESCRIPTION HARDNESS REGULATORY STERILIZATION CHARACTERISTICS Versalloy™ HC 9210-45N 45A USP Class VI EtO Good processability, HC 9210-55N 55A USP Class VI EtO Good processability, HC 9210-70N 70A USP Class VI EtO Good processability, HC 9220-43N 43A USP Class VI, ISO 10993-4/5 EtO Extrusion grade, high temperature resistance Versaflex™ HC 2110-35N 34A FDA, USP Class VI, ISO 10993 Autoclave EtO radiation Resealing, elevated comp set Versaflex™ HC 2110-57B 57A FDA, USP Class VI, ISO 10993 Autoclave EtO radiation Low stiction VERSAFLEX™ CL AND DYNAFLEX™ TPEs HIGH CLARITY GRADES WITHOUT PLASTICIZERS • Water clear grades formulated without phthalate plasticizers • Meets medical regulatory USP Class VI and ISO 10993-4,5 • Food contact and FDA compliant • Autoclave and radiation stable • Low extractable • High clarity (Haze 50 4.1, 100 4.5, 100 4, 70 6, 70 Tensile Modulus (MPa) 2200 2700 2600 2350 1820 1820 Flexural Strength (MPa) 80 90 104 86 68 68 Flexural Modulus (MPa) 2500 2700 2500 2300 1980 1590 HDT: 0.45, 1.8 (MPa) 110, 80 90, 80 100, 89 123, 100 123, 64 100, 70 UL-94 Rating @ 3.0 mm 5VA V-0 5VA V-0 HB V-0 UL-94 Rating @ 1.5 mm V-0 V-0 5VB V-0 HB V-0 UL-94 Rating @ 0.75 mm V-1 V-2 V-0 None None V-2 COMPETITIVE MATERIAL COMPARISON ENGINEERED POLYMER FORMULATIONS FOR HEALTHCARE TRILLIANT™ HC THERMOPLASTICS The family of Trilliant™ HC high-performance thermoplastics is formulated to meet the growing challenges of medical devices and equipment. MATERIAL DESCRIPTION BASE RESIN Trilliant™ HC2020 Copolyester Trilliant™ HC8910/8920 Polyketone/ABS blend Trilliant™ HC2120 Tritan Trilliant™ HC3120 PC Trilliant™ HC5210 PP Trilliant™ HC6010 PA6 Trilliant™ HC6610 PA66 Trilliant™ GRV-NP-110-W PA12 TRILLIANT™ HC THERMOPLASTICS • Chemically resistant replacement for FR PC/ABS, FR PC/PET & FR COPE, providing UL 94 Yellow Card V-0 flame rating at 1.5 mm, V-1 at 0.75 mm thicknesses for a broad color spectrum • Outperforms PC/ABS, PC/PET and COPE in resistance to common disinfectants • Retains tensile strength after 72-hour exposure to common hospital disinfectants, and shows better long-term chemical resistance as compared to PC blends and COPE • Exhibits good impact and temperature resistance • Available in natural grades, standard medical colors, or custom pre-colored products • Medical device housings • MRI, X-ray, CT scanner components • Surgical instruments such as staplers, dissectors, scissors • Auto-injector pen TRILLIANT™ HC ELECTRICALLY CONDUCTIVE FORMULATIONS • Consistent conductivity ensures repeatable part performance and minimizes failures related to inconsistent electrical conductivity • High flow and easy processing facilitate filling of thin wall parts and multiple cavity tools, which enable faster cycle times and lower per-unit part costs • Superior durability reduces breakage and resultant scrap related costs • Less tendency to flash results in improved appearance and less fluid retention in or on the tip, thus driving greater accuracy and less potential for cross-contamination • High strength produces parts with greater stiffness and warp resistance, again minimizing scrap-related costs • Conductive pipette tips TEST TEMS SPECIFIC GRAVITY MELT FLOW RATE (230OC, 2.16KG) TENSILE FLEXURAL FLEXURAL MODULUS IMPACT STRENGTH NOTCHED, IZOD SURFACE RESISTIVITY Method ASTM D-792 ASTM D-1238 ASTM D-638 ASTM D-790 ASTM D-790 ASTM D-256 ASTM D-257 Unit -- g/10min MPa MPa MPa J/m Ohms/sq. ST5200-8030 ESD BK001 1 5 27 52 1980 42 E3 ST5200-8035 ESD BK001 1 20 22 37 1460 150 E3 +86.21.60284888 www.avient.com Copyright © 2021, Avient Corporation.

OSHA established a date of June 1, 2015 for those required to generate SDSs for their formulation or mixture products to start using the new GHS format. Distributors have until December 1, 2015 to implement the same changes. Complete implementation for suppliers and employers will be required by December 1, 2018.

Clause 1, Clause 2, Clause 3, Clause 6, Clause 7; ii. The details for “Table 1: Parties” shall be set out in Appendix to Schedules 2(a), (b), and (c), Annex 1; b. Entering into this Addendum 1.

KEY PROPERTIES AND PERFORMANCE FR GRADES H GRADES PEEK GRADES LCP GRADES FLEX GRADES PROPERTIES CONDITION ISO UNIT PPE400FR PPE700FR PPE950FR PPE1200FR H1500HF H2300HF PEEK700 PEEK900 PEEK1000 PEEK1200 LCP650 LCP800 LCP950 FLX400 FLX700 FLX1100 Dielectric Constant (Dk) 2.4 GHz 4.0 7.0 9.5 12.0 15.0 23.0 7.0 9.0 10.0 12.0 6.5 8.0 9.5 4.0 7.0 11.0 Loss Tangent (Df) 2.4 GHz 0.0030 0.0039 0.0042 0.0045 0.0010 0.0037 0.0024 0.0025 0.0024 0.0027 0.0043 0.0045 0.0047 0.0010 0.0009 0.0012 Density 1183 g/cm3 1.44 1.97 2.20 2.50 2.60 3.40 1.94 2.20 2.30 2.40 2.00 2.15 2.30 1.52 1.93 2.50 Melt Flow Index (MFI) 5 kg, 300 °C (unless noted) 1113 g/10 min 17 12 13 5 5 8 15 @ 380 °C 13 @ 380 °C 10 @ 380 °C 6 - - - 11 @ 230 °C 2 @ 230 °C 0.3 @ 230 °C Tensile Strength at Break 23 °C/73 °F 527 MPa 47 52 44 45 23 40 64 62 65 67 75 80 75 11 17 25 Flexural Modulus 23 °C/73 °F 178 MPa 3100 4500 - 9300 2100 5000 6200 7600 9200 11000 8000 8500 8500 1400 1600 2900 Unnotched Izod 23 °C/73 °F 180 kJ/m2 NB 42 20 9 17 10 28 25 18 15 31 20 12 NB NB NB -20 °C/-4 °F 180 kJ/m2 - - - - 17 10 - - - - - - - - - Notched Izod 23 °C/73 °F 180 kJ/m2 14 6 4 3 5 4 6 4 4 4 10 6 4 59 23 13 -20 °C/-4 °F 180 kJ/m2 - - - - 5 4 - - - - - - - - - - STANDARD GRADES RADOME GRADES PROPERTIES CONDITION ISO UNIT PPE260 PPE300 PPE320 PPE350 PPE400 PPE440 PPE500 PPE650 PPE800 PPE950 PPE1200 RS260 RB260 RS265FR Dielectric Constant (Dk) 2.4 GHz 2.6 3.0 3.2 3.5 4.0 4.4 5.0 6.5 8.0 9.5 12.0 2.6 2.6 2.7 Loss Tangent (Df) 2.4 GHz 0.0009 0.0009 0.0010 0.0009 0.0009 0.0009 0.0009 0.0009 0.0009 0.0009 0.0010 0.0009 0.0012 0.0032 Density 1183 g/cm3 1.07 1.18 1.21 1.27 1.43 1.50 1.62 1.86 2.10 2.20 2.40 1.06 1.08 1.09 Melt Flow Index (MFI) 5 kg, 300 °C 1113 g/10 min 15 15 16 14 14 14 15 11 10 4 2 21 16 25 Tensile Strength at Break 23 °C/73 °F 527 MPa 40 45 47 50 50 48 45 43 37 37 36 50 42 52 Flexural Modulus 23 °C/73 °F 178 MPa 2700 2400 2000 2600 2800 2700 2600 2600 2300 2600 2600 2200 2200 2600 Unnotched Izod 23 °C/73 °F 180 kJ/m2 NB NB NB NB NB NB NB NB 50 28 24 NB NB NB -20 °C/-4 °F 180 kJ/m2 NB NB NB NB NB NB NB 50 47 27 25 NB NB NB Notched Izod 23 °C/73 °F 180 kJ/m2 8 55 69 35 22 20 15 9 8 5 4 19 14 11 -20 °C/-4 °F 180 kJ/m2 8 15 20 14 12 10 9 8 8 5 4 10 12 10 PREPERM™ SERIES PROPERTIES CONDITION ISO UNIT 8027 8025 8037 8019 8028 8026 8044 8029 8041 8045 8048 8036 8056 8031 Dielectric Constant (Dk) 1 GHz, 23 °C 3.0 3.1 3.4 3.6 3.8 4.4 4.8 5.3 5.4 5.9 6.0 7.0 7.3 9.0 Loss Tangent (Df) 1 GHz, 23 °C 0.0012 0.0012 0.0008 0.0010 0.0010 0.0010 0.0004 0.0008 0.0006 0.0002 0.0006 0.0007 0.0002 0.0007 Density 1183 g/cm3 1.25 1.26 1.35 1.39 1.45 1.59 1.72 1.75 1.79 1.89 1.88 2.06 2.086 2.25 Melt Flow Index (MFI) 5 kg, 300 °C 1113 g/10 min 16 19 10 11 15 13 10 10 15 15 19 10 18 4.7 Tensile Strength at Break 23 °C/73 °F 527 MPa 59 54 54 62 59 54 52 58 52 45 49 45 37 38 Flexural Modulus 23 °C/73 °F 178 MPa 2780 2560 2850 3060 3350 3700 3157 4300 4320 3137 4150 3370 2560 4200 Notched Izod 23 °C/73 °F 180 kJ/m2 15.3 14 14.8 14 12.6 10.4 9.9 8.6 7.4 7.9 6.6 7.1 6.2 6.8 EDGETEK™ 7600 SERIES Copyright © 2021, Avient Corporation.

SELF-SERVICE 1. Your colors can be consistently reproduced from any Avient facility worldwide. 1 2 VISIT ONE OF OUR SELECT FACILITIES Alternatively, you can visit one of our global Select development facilities and work with one of our experts to create your color, produce and approve samples all in the same day.

PRODUCTS APPLICATIONS DESCRIPTION/BENEFITS EXCELITE PF-1 PVC sheet for digital print or trimboard; Fine cell structure able to target low density: improves consistency and control over foaming process FOAM ADDITIVE-54 PVC sheet for digital print or trimboard; Finer cell structure than PF-1 promotes ultra smooth surface finish; improves consistency and control over foaming process PF-1E & FA-54E ADDITIVES PVC sheet for digital print or trimboard; Enhanced run time formulation reduces die lip build-up in PVC processes, leading to longer production run times FOAM ADDITIVE-33 CaZN formulations for PVC sheet, profile, or trimboard Promotes finer cell structure, higher cell density, and surface quality in CaZN PVC dryblends FOAM ADDITIVE-77 HDPE sheet & plastic lumber Industry-leading cell structure and cell density; achieves lower density without sacrificing quality; self-nucleating and able to increase extruder output rates up to 15% FOAM ADDITIVE-85 Endothermic foam or nucleating additive for olefin and styrene polymers; plastic lumber, sheet applications and food packaging products Can be used as a CFA or nucleating additive; nucleating capabilities promote fine cell structure and high cell density; achieves greater density reductions with more consistency and control FOAM ADDITIVE-37 HDPE sheet & plastic lumber Good cell structure and cell density in HDPE lumber; greater consistency and control over foaming process EXCELITE CAN IMPROVE PRODUCTION EFFICIENCY • The process operator has full control of density • Minimizes product rejection due to unnecessarily high/low density • Production should consistently target the bottom of the density specification • Enables control over the reintroduction of regrind or reprocessed materials as a feedstock • Enables the consistent foaming of products using higher percentages of regrind • Carrier selection can promote longer run times, enabling increased line productivity through less plate-out or material build-up on die lips EXCELITE CAN IMPROVE SURFACE FINISH Excelite additives creates a fine, consistent cell structure within the extruded polymer, which determine the surface roughness.